Quartz PropertiesQuartz (GE124) The applications for quartz are endless where optical clarity, chemical and thermal resistance ,insulation, and hardness.
If you have any problems viewing table, download image version
Quartz Properties
Quartz
The applications for quartz are endless where optical clarity, chemical and thermal resistance and insulation, and hardness are required. Commonly used in the semiconductor world and the lighting industry.Properties
|
Units
|
Test
|
Value
|
|---|---|---|---|
Physical
|
|||
Chemical Formula
|
SiO2
|
||
Density, r
|
g/cm3
|
ASTM C20
|
2.21
|
Color
|
-
|
-
|
white/ transparent
|
Crystal Structure
|
-
|
-
|
hexagonal
|
Water Absorption
|
% @R.T.
|
ASTM C373
|
0.0
|
Hardness
|
Moh's
|
-
|
7
|
Hardness
|
knoop (kg/mm2)
|
Knoop 100g
|
> 600
|
Mechanical
|
|||
Compressive Strength
|
MPa @ R.T.
|
ASTM C773
|
650 - 1100
|
Tensile Strength
|
MPa @ R.T.
|
ACMA Test #4
|
48
|
Modulus of Elasticity
(Young's Mod.) |
GPa
|
ASTM C848
|
70
|
Flexural Strength (MOR)
|
MPa @ R.T.
|
ASTM F417
|
80
|
Poisson's Ratio, u
|
ASTM C818
|
0.17
|
|
Fracture Toughness, KIc
|
MPa x m1/2
|
Notched Beam Test
|
-
|
Thermal
|
|||
Max. Use Temperature
(* denotes inert atm.) |
ºC
|
No load cond.
|
1200
|
Thermal Shock Resistance
|
DT (ºC)
|
Quenching
|
> 1400
|
Thermal Conductivity
|
W/m-K @ R.T.
|
ASTM C408
|
1.4
|
Coefficient of Linear Thermal Expansion, al
|
mm/m-ºC (~25ºC
through ±1000ºC)
|
ASTM C372
|
0.45
|
Specific Heat, cp
|
cal/g-ºC @ R.T.
|
ASTM C351
|
0.16
|
Electrical
|
|||
Dielectric Constant
|
1MHz @ R.T.
|
ASTM D150
|
3.8
|
Dielectric Strength
|
kV/mm
|
ASTM D116
|
25 - 40
|
Electrical Resistivity
|
Wcm @ R.T.
|
ASTM D1829
|
6 x 1010
|
*Although we have no reason to doubt the accuracy of the data presented, Ferro-Ceramic Grinding Inc. offers this information for comparison only, and disclaims any and all liability from error, omissions or inaccuracies, such that it does not constitute a warranty or representation for which we shall assume legal responsibility.